Aluminum 6082-T651

Material type: Metal, Corrosion resistance, Non-magnetic

Aluminum 6082-T651 (CNC) has very similar composition and properties to 6061, with slightly higher tensile strength. Compliant with British Standards.

Process compatibility

CNC Milling CNC Turning

Material Color

Silver white

Material advantages

It has high strength, excellent machinability and good weldability, and is suitable for the aerospace, automotive and construction industries.

Material shortcomings

The weld has high sensitivity to cracks and limited formability. It is not suitable for parts with extremely high loads and high rigidity requirements.

Recommended description

The 6082-T651 has a higher strength than 6061-T6. It undergoes pre-stretching to eliminate the residual stress from quenching, and the CNC precision processing of thick plates ensures good dimensional stability. It has excellent corrosion resistance and anodizing performance. Compared with 7075, its cost performance is superior. It is suitable for high-precision medium-high load large plate, thick plate structural components and tooling fixtures.

Properties

Name
Ultimate tensile strength	275-320 MPa
Yield strength	240-270 MPa
Young's modulus (modulus of elasticity)	69 – 70 GPa
Elongation at break	6 - 10 %
Corrosion resistance	High
Magnetism	Non-magnetic
Weldability	High
Maximum service temperature	150 °C
Thermal expansion coefficent	23.4 ×10⁻⁶ /℃
Thermal conductivity	170 W/(m⋅°C)
Electrical resistivity	3.5 μΩ·cm
Post-Processing	NA
Anodizing compatibility	Suitable