HP-PA-12
Material type: Plastic, High strength, Impact resistant
HP-PA has a variety of material properties that can meet the requirements of different scenarios. The parts have excellent impact resistance, can be used repeatedly for a long time, have excellent heat resistance, and do not deform.
Process compatibility
Material Color
Dark black (spray paint)
Material advantages
Good impact resistance, the parts can be used repeatedly for a long time, excellent toughness, and will not deform when heated.
Material shortcomings
The surface is slightly grainy.
Recommended description
Nylon materials can be used to directly produce various parts and shells with excellent performance, which can reduce weight and increase quality under the premise of optimized structural design.
Properties
Name | |
---|---|
Powder melting point (DSC) | 187°C / 369°F |
Particle size | 60 µm |
Bulk density of powder | 0.425 g/cm3 / 0.015 lb/in3 |
Density of parts | 1.01 g/cm3 / 0.036 lb/in3 |
Tensile strength, max load - XY | 48 MPa/6960 psi |
Tensile strength, max load - Z | 48 MPa/6960 psi |
Tensile modulus - XY | 1800 MPa/261 ksi |
Tensile modulus - Z | 1800 MPa/261 ksi |
Elongation at break - XY | 20% |
Elongation at break - Z | 15% |
Flexural strength (@ 5%) - XY | 65 MPa/9425 psi |
Flexural strength (@ 5%) - Z | 70 MPa/10150 psi |
Flexural modulus - XY | 1730 MPa/251 ksi |
Flexural modulus - Z | 1730 MPa/251 ksi |
Izod impact notched (@ 3.2 mm, 23°C), XYZ | 3.5 kJ/m2 |
Thermal properties Heat deflection temperature (@ 0.45 MPa, 66 psi), XY | 175°C/347°F |
Heat deflection temperature (@ 0.45 MPa, 66 psi), Z | 175°C/347°F |
Heat deflection temperature (@ 1.82 MPa, 264 psi), XY | 95°C/203°F A |
Heat deflection temperature (@ 1.82 MPa, 264 psi), Z | 95°C/203°F |
* Nylon parts will have a slight graininess, and more post-processing steps are needed. Please confirm with your sales rep.
Common applications
Customer reviews
3d-printing resources for engineers
Article
[Case Study] 3D printing promotes pump and valve technology upgrades and accelerates new product development
By
Eric
Oct 20,2023
Article
3D printing parts common quality problem solving guide
By
Guan Nin
Sep 12,2023
Article
Science Robotics: BASF CARA and the University of California team up to create 3D printed soft robotics
By
Justway Support Team
Jul 31,2023
Article
Understanding the Basics: A Guide to research on 3D Printing TPU Materials
By
Justway Support Team
Jul 14,2023